二硫化钼纳米片用于修饰微生物燃料电池阳极的研究

利用简单的一步水热法制备了MoS2纳米片并用于修饰不锈钢纤维毡阳极(MoS2-SSFF),与未修饰不锈钢纤维毡阳极(SSFF)和多壁碳纳米管修饰阳极(CNT-SSFF)进行了对比研究。装配MFC运行的测试结果表明,MoS2-SSFF/MFC的功率密度为714 m W/m2,略高于CNT-SSFF/MFC的功率密度693 m W/m2,远高于未修饰SSFF/MFC的功率密度197 m W/m2。利用扫描电子显微镜(SEM)观察到MoS2纳米片呈簇状附着于MoS2-SSFF电极表面,显著增加了电极的比表面积。MoS2纳米片修饰改善了SSFF阳极的生物相容性,修饰电极在循环伏安测试(CV)中表现出良好的氧化还原性能。水热法制备的MoS2纳米片用于修饰阳极是一种高效、经济、简单的阳极修饰方法。     

Fatigue damage study of cold metal transition fusion-brazed aluminium/steel dissimilar joints

ABSTRACT

An aluminium/steel CMT-welded joint is mainly composed of fusion zone (FZ), interfacial intermetallic compound (IMC) zone, and heat-affected zone (HAZ). IMC and FZ are the weakest link in the welded joint. The fatigue fracture indicates that the lattice distortion caused by the lattice mismatch of Fe₂Al₅ and Fe is more likely to engender dislocation slipping and cracks easily nucleate during the fatigue testing. The hysteresis loop is shifted to the right, which indicating that the specimen experiences a ratcheting effect. In the high-stress condition, the cyclic hardening induced by the ratcheting strain is much stronger than that in the lower stress condition, which improves the fatigue life of the materials.     

淬火处理对轧辊用高硼高速钢组织和性能的影响

利用光学显微镜、扫描电镜、X射线衍射、硬度计及MM-200磨损试验机,研究了淬火温度对轧辊用高硼高速钢显微组织和性能的影响。结果表明,高硼高速钢的铸态组织由马氏体、铁素体、珠光体和沿晶界呈连续网状分布的共晶硼碳化物组成,共晶硼碳化物主要是M2B和M7(C,B)3;随着淬火温度的升高,基体全部转变成为马氏体,并有二次硼碳化物M23(C,B)6析出;高硼高速钢的硬度和耐磨性随着淬火温度的升高而明显增加,在1150℃淬火时硬度最高、耐磨性最好。     

国内外帘线钢盘条夹杂物检验方法的介绍

围绕国内外帘线钢盘条的夹杂物检验方法，对国内外4种主要典型帘线钢盘条夹杂物检验方法进行了详细介绍及比较，了解了4种检验方法的技术特点，总结了帘线钢盘条夹杂物检验方法的核心要点，尤其对这4种检验方法中所涉及的试样取样面积、夹杂物的类型名称、光学显微镜下不同类型夹杂物的特征形貌进行了识别，阐明了做好帘线钢盘条夹杂物检验和质量控制的价值和意义。     

双相不锈钢表面激光熔覆钴基合金组织和性能研究

目的提高2205双相不锈钢的耐磨性和耐腐蚀性能。方法采用激光熔覆技术,在2205双相不锈钢基体表面制备钴基合金熔覆层。用X射线衍射仪、光学显微镜检测钴基合金熔覆层的相组成和显微组织,用能谱仪测定熔覆层和基体界面区域的Fe和Cr元素分布,确定熔覆层界面过渡区域的宽度。用显微硬度计和湿砂磨粒磨损试验机,测试熔覆层硬度和耐磨性能。采用扫描电镜观察摩擦表面的磨损特性,分析钴基合金熔覆层的磨损机理。用电化学工作站测试熔覆层的电化学腐蚀特性,并用2205双相不锈钢作为对比试样做相应的性能试验。结果熔覆层由γ-Co固溶体和少量的Cr7C3、Cr2Ni3化合物相组成,界面处的熔覆层相组织是少量的平面晶和胞状晶,其他区域是发达的树枝晶。由于熔覆层由多道搭接和多层熔覆形成,树枝晶生长有方向性,但不是成固定的方向,并出现明显的分层现象。熔覆层过渡区范围为50μm左右,熔覆层平均显微硬度达477HV(0.1),远高于2205双相不锈钢基体(265HV(0.1))。当磨程达到3354m时,熔覆层的质量损失仅为10.3 mg,约为基体质量损失的1/3。在3.5%NaCl溶液中,熔覆层具有较高的极化电阻与电荷转移电阻和较小的自腐蚀电流。结论熔覆层组织致密,无气孔、裂纹等缺陷,与基体呈良好的冶金结合,钴基合金熔覆层具有良好的耐磨粒磨损性能和耐腐蚀性能。     

热轧双相钢生产现状、存在问题及发展趋势浅析

介绍了国内外热轧双相钢的发展现状；对热轧双相钢的成分体系和关键生产工艺进行了总结，指出了目前热轧双相钢在生产过程中存在的问题；提出了未来热轧双相钢的主要发展方向为低成本、高强度、低负荷、高表面质量和“以热代冷”。     

355 MPa级转向架构架用钢连续冷却转变行为

高速动车组转向架构架对高速动车组的运行品质、行车安全起到至关重要的作用。为向355 MPa级转向架构架用钢的工业试制提供指导，在Gleeble-3800热模拟试验机上进行了热模拟试验，结合热膨胀法和金相-硬度法，绘制了355 MPa级转向架构架用钢动态连续冷却转变曲线，研究了试验钢在连续冷却条件下的显微组织演变规律。结果表明，冷速小于1 ℃/s时，其组织主要为多边形铁素体和珠光体；冷速大于5 ℃/s时，贝氏体类组织快速增加；冷速达到50 ℃/s时，为板条贝氏体组织。因此，对于355 MPa级转向架构架用钢，冷速控制在1~5 ℃/s较为适宜，其组织主要由比例适中软硬性相结合的铁素体、珠光体和贝氏体构成，可以获得优良的强韧性匹配。     

1 200 MPa级冷轧先进高强钢轧制稳定性的分析及控制

针对1 200 MPa级冷轧先进高强钢轧制不稳定问题,对热轧原料组织性能均匀性、冷轧压缩比、冷连轧机组轧制策略等进行了分析。结果表明,热轧工序投入边部加热器,采用分段冷却等手段,可有效降低热轧原料头尾部组织性能差异,保证通卷性能均匀,进而保证通卷轧制过程稳定;通过优化冷连轧机组压缩比,可有效降低材料本身的加工硬化强度,进而避免连轧机组后面机架的轧制超负荷情况;通过优化冷连轧机组轧制策略,可保证轧制过程中各机架均匀变形,避免出现轧制力差异较大的情况,进而保证轧制过程稳定。采用上述措施,1 200 MPa级冷轧先进高强钢轧制力控制在约15 000 kN,厚度精度控制在±0.06 mm以内,可保证该级别高强钢的稳定轧制。     

Effect of Indirect Transformation of Retained Austenite During Tempering on the Charpy Impact Toughness of a Low-Alloy Cr-Mo-V Steel

A modified tempering treatment has been designed in order to avoid the direct transformation of retained austenite (Ar) during tempering of a low-alloy Cr-Mo-V steel. Instead of the direct transformation of Ar into ferrite and M₂₃C₆ carbides during conventional tempering at 700 °C, transformation into aggregate of ferrite and cementite has been forced by a pre-tempering at 455 °C before conventional tempering. Experiments have been performed on specimens quenched with cooling rates 1.5, 3 and 12 °C/s, providing different types of Ar within the as-quenched microstructures. The results show that the tempering modification does not improve the Charpy impact toughness at the highest quenching rate of 12 °C/s, where the specimens cannot incur cleavage cracking induced from fine and discontinuous M₂₃C₆ carbides along lath interfaces. For the lowest quenching rate 1.5 °C/s, the Charpy impact toughness can be improved, and the failure is dominated by carbide aggregates, which originate from the decomposed products of blocky Ar. This is because the tempering modification effectively suppresses the formation of coarse M₂₃C₆ carbides at interfaces between the carbide aggregate and bainitic matrix, thereby resulting in a relatively homogeneous distribution of M₂₃C₆ carbides inside carbide aggregates. Therefore, the tempering modification is recommended for large-scale forgings, in which relatively high quenching rates are difficult to achieve.     

Ultra-thin Laminated Metal Composites with Ultra-high Strength and Excellent Soft Magnetic Properties

Structural metallic materials with excellent functional performance and lightweight features have always been the goal of material scientists' pursuit.In this work,laminated metal composites of different thicknesses(less than 0.4 mm) composed of structural materials with great differences in deformation ability were successfully fabricated via a novel processing procedure.Ultra-high strength and excellent soft magnetic properties were combined perfectly in the ultra-thin and super-light laminated metal composite strips due to unique structural design and essential attributes of the initial materials.These results emphasize the significant potential application value of the ultra-thin laminated metal composites in the field of structural and functional integration.